D – 97 Standard Test Method for Nondestructive Measurement of Dry Film Thickness of Applied Organic Coatings Over Concrete Using an Ultrasonic Gage . Designation: D − 08Standard Test Method for Nondestructive Measurement of Dry Film Measurements may be made on field ASTM Test Methods. Designation: D − Standard Test Method for. Nondestructive Measurement of Dry Film Thickness of Applied Organic Coatings Using an.

Author: Nejora Tojashicage
Country: Martinique
Language: English (Spanish)
Genre: Career
Published (Last): 28 March 2010
Pages: 280
PDF File Size: 11.38 Mb
ePub File Size: 4.12 Mb
ISBN: 519-6-20519-649-1
Downloads: 18194
Price: Free* [*Free Regsitration Required]
Uploader: Shajin

To be able to compare results obtained by different operators, it is essential to measure film thickness carefully. Measurements may be made on field structures, on commercially manufactured products, or on laboratory test specimens.

These types of gages can accurately measure the dry film thickness of organic coatings on a variety of substrates such as concrete, wood, wallboard, plastic, fiber composites and metal. While this is a destructive test method, it will provide an alternative test method to ensure measurements made in accordance with this test method are in the correct range.

Referenc Referenced ed Documents Documents 2.

ASTM D6132 – 13(2017)

Thank you for interesting in our services. Please help us to share our service with your friends. These seven coated panels were described as the following: For best accuracy, each instrument should be checked against a known thickness of the particular coating being measured and adjusted if necessary. For rough coatings, a glycol gel is best, provided it is not a contaminant for the coating to be measured.

  AS BRUMAS DE AVALON VOL 3 PDF

Other liquids such as liquid soap may be used. Summ Summary ary of Test Test Method 3. A number in paren parenthese thesess indicates the year of last reappr reapproval. Coatings d61132 be applied within certain minimum and maximum thickness tolerances in order that they can fulfill their intended function.

All laboratories reported two replicate test results for every panel with each instrument. Water is ideal for smooth, thin astn. Precision and Bias4 Each of eight laboratories tested seven different coated panels using two types of instrumentation.

Last previously edition approved in as D — The instrument may allow a user adjustment to prevent this. Please copy and paste this embed script to where you want to embed Embed Script.

Hold the probe steady during the measurement. Size px x x x x Therefore the reference standard should be smooth.

Historical Version s – view previous versions of standard. A rough surface has a tendency to scatter d61332 ultrasonic pulse and odd readings may occur occasionally. Select the method most appropriate for the material being tested. The instrument must be placed directly on the coating surface to take a reading.

ASTM Dpdf – Free Download PDF

The instrument’s ability to detect a distinct interface between the coating and the substrate may be impeded if the coating and the substrate d61332 of similar composition, density or attenuation or if the coating is non-homogeneous. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Permission rights to photocopy the standard may also be secured from the ASTM website www.

  ALIGERA TU EQUIPAJE PDF

A thickness range of 0. Originally approved in Current edition approved July 1, Please fill this form, we will try to respond as soon as possible. Approved July 1, The travel time is converted astj a thickness reading.

We need your help to maintenance this website. Referenced Documents purchase separately The documents listed below are v6132 within the subject standard but are not provided as part of the standard.

No other units of measurement are included in this standard. We need your help! We are a non-profit group that run this website to share documents. UV cured coating on hickory Panel 2: In addition to potential performance deficiencies, it is uneconomical to apply more material than necessary when astk large areas such as floors and walls.

Some instruments have the ability to detect and measure the individual layer thicknesses in a multi-layer system.

Some instruments have the ability to detect and measure the individual layer thicknesses in a multi-layer system. Link to Active This link will always route to the current Active version of the standard.

No other units of measurement are included in this standard.